Synthesis and Luminescence Properties of Zn2GeO4 Nanorods
Yang, Y.; Y. Cong; Z. M. Zhu; C. Guo; Z. Zhang; Z. W. Wang and J. H. Zhang
2017
Source PublicationChinese Journal of Inorganic Chemistry
Volume33Issue:10
AbstractZn2GeO4 nanorods were synthesized through a facile hydrothermal method at different pH values, and the morphology and luminescence properties of Zn2GeO4 nanorods were systematically studied. The SEM results indicate that the particle sizes decreased with the increased in pH values from micro- to nano-size, and the length of Zn2GeO4 nanorods (L=200 similar to 500 nm) can be controlled through the pH values. Two emission bands centered at 450 and 530 nm were observed which are associated with different native defects in Zn2GeO4 nanocrystals.
Indexed Bysci ; ei
Language英语
Document Type期刊论文
Identifierhttp://ir.ciomp.ac.cn/handle/181722/59386
Collection中科院长春光机所知识产出
Recommended Citation
GB/T 7714
Yang, Y.,Y. Cong,Z. M. Zhu,et al. Synthesis and Luminescence Properties of Zn2GeO4 Nanorods[J]. Chinese Journal of Inorganic Chemistry,2017,33(10).
APA Yang, Y.,Y. Cong,Z. M. Zhu,C. Guo,Z. Zhang,&Z. W. Wang and J. H. Zhang.(2017).Synthesis and Luminescence Properties of Zn2GeO4 Nanorods.Chinese Journal of Inorganic Chemistry,33(10).
MLA Yang, Y.,et al."Synthesis and Luminescence Properties of Zn2GeO4 Nanorods".Chinese Journal of Inorganic Chemistry 33.10(2017).
Files in This Item: Download All
File Name/Size DocType Version Access License
Synthesis and Lumine(1345KB)期刊论文作者接受稿开放获取CC BY-NC-SAView Download
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Yang, Y.]'s Articles
[Y. Cong]'s Articles
[Z. M. Zhu]'s Articles
Baidu academic
Similar articles in Baidu academic
[Yang, Y.]'s Articles
[Y. Cong]'s Articles
[Z. M. Zhu]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Yang, Y.]'s Articles
[Y. Cong]'s Articles
[Z. M. Zhu]'s Articles
Terms of Use
No data!
Social Bookmark/Share
File name: Synthesis and Luminescence Properties.pdf
Format: Adobe PDF
This file does not support browsing at this time
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.