Preparation and optical properties of Er3+-doped gadolinium borosilicate glasses | |
其他题名 | 论文其他题名 |
Sun J. T.; Zhang J. H.; Chen B. J.; Lu S. Z.; Ren X. G.; Wang X. J. | |
2005 | |
发表期刊 | Journal of Rare Earths |
ISSN | 1002-0721 |
卷号 | 23期号:2页码:157-161 |
摘要 | Er3+-doped Gd2O3-SiO2-B2O3-Na2O glasses were prepared, and formation range of glass of Gd2O3 - SiO2 -B2O3 system was experimentally obtained. It is found that the glass phase can be formed only when the content of SiO2 is 0-50% (molar fraction), Gd2O3 is 0-30% (molar fraction) and B2O3 is above 20% (molar fraction) in this glass system. The glass can also be obtained but becomes translucent at the contents of 60% (molar fraction) SiO2 and 30% Gd2O3, or at the contents of 60% (molar fraction) SiO2 and 30% (molar fraction) B2O3. There is no glass phase formed in other glass components. Glass forming ability for Gd,03 content of 10%, was characterized by the value of,8, the parameter of crystallization tendency, which is 0.32-1.76, obtained from the differential thermal analysis. The absorption and emission cross section, the J-O parameters Omega t((2,4,6)) and radiative transition probabilities were calculated by using the theory of McCumber and Judd-Ofelt. The emission properties at 1.5 mu m of the samples are discussed with the product of full width at half maximum and stimulated emission cross section. It can be seen that the value of the FWHM x sigma(e)(peak) product in the prepared glass is more than those of germanate, silicate and phosphate glasses. Furthermore, the maximum value of the product among these glasses reported in this work is close to that of oxyfluoride silicate glass. Therefore, the Er3+-doped gadolinium borosilicate glass in this paper is a candidate for broadband erbium doped fiber amplifiers. |
收录类别 | SCI ; EI |
语种 | 英语 |
文献类型 | 期刊论文 |
条目标识符 | http://ir.ciomp.ac.cn/handle/181722/26807 |
专题 | 中科院长春光机所知识产出 |
推荐引用方式 GB/T 7714 | Sun J. T.,Zhang J. H.,Chen B. J.,et al. Preparation and optical properties of Er3+-doped gadolinium borosilicate glasses[J]. Journal of Rare Earths,2005,23(2):157-161. |
APA | Sun J. T.,Zhang J. H.,Chen B. J.,Lu S. Z.,Ren X. G.,&Wang X. J..(2005).Preparation and optical properties of Er3+-doped gadolinium borosilicate glasses.Journal of Rare Earths,23(2),157-161. |
MLA | Sun J. T.,et al."Preparation and optical properties of Er3+-doped gadolinium borosilicate glasses".Journal of Rare Earths 23.2(2005):157-161. |
条目包含的文件 | 下载所有文件 | |||||
文件名称/大小 | 文献类型 | 版本类型 | 开放类型 | 使用许可 | ||
PreparationandOptica(622KB) | 开放获取 | -- | 浏览 下载 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论