Multifunctional Zn0.99-xMn0.01CuxS nanowires: Structure, luminescence and magnetism | |
其他题名 | 论文其他题名 |
Cao J.; Yang J. H.; Zhang Y. J.; Yang L. L.; Wang Y. X.; Wang D. D.; Gao M.; Liu Y.; Liu X. Y.; Xie Z. | |
2010 | |
发表期刊 | Materials Research Bulletin |
ISSN | 0025-5408 |
卷号 | 45期号:6页码:705-709 |
摘要 | The wurtzite-type Zn0.99-xMn0.01CuxS (x = 0, 0.003, 0.01) nanowires were prepared by a simple hydrothermal method at 180 C The structure and morphology of the samples were characterized by X-ray diffraction (XRD). X-ray absorption fine structure (XAFS), transmission election microscopy (TEM), high-resolution transmission electron microscopy (HRTEM), field emission scanning electron micrograph (FESEM) and X-ray photoelectron spectrum (XPS). The results showed that both the Mn2+ and Cu2+ ions substituted for the Zn2+ sites in the host ZnS The ethylenediamine-mediated template was observed, which was used to explain the growth mechanism of the nanowires The color-tunable emission can be obtained by adjusting the concentrations of Mn2+ and Cu2+ ions The ferromagnetism was observed around room temperature Crown Copyright (C) 2010 Published by Elsevier Ltd All rights reserved |
收录类别 | SCI ; EI |
语种 | 英语 |
文献类型 | 期刊论文 |
条目标识符 | http://ir.ciomp.ac.cn/handle/181722/26124 |
专题 | 中科院长春光机所知识产出 |
推荐引用方式 GB/T 7714 | Cao J.,Yang J. H.,Zhang Y. J.,et al. Multifunctional Zn0.99-xMn0.01CuxS nanowires: Structure, luminescence and magnetism[J]. Materials Research Bulletin,2010,45(6):705-709. |
APA | Cao J..,Yang J. H..,Zhang Y. J..,Yang L. L..,Wang Y. X..,...&Xie Z..(2010).Multifunctional Zn0.99-xMn0.01CuxS nanowires: Structure, luminescence and magnetism.Materials Research Bulletin,45(6),705-709. |
MLA | Cao J.,et al."Multifunctional Zn0.99-xMn0.01CuxS nanowires: Structure, luminescence and magnetism".Materials Research Bulletin 45.6(2010):705-709. |
条目包含的文件 | 下载所有文件 | |||||
文件名称/大小 | 文献类型 | 版本类型 | 开放类型 | 使用许可 | ||
Cao-2010-Multifuncti(465KB) | 开放获取 | -- | 浏览 下载 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论