Ultraviolet photodetector fabricated from metal-organic chemical vapor deposited MgZnO | |
其他题名 | 论文其他题名 |
Zhao C. Y.; Wang X. H.; Zhang J. Y.; Ju Z. G.; Shan C. X.; Yao B.; Zhao D. X.; Shen D. Z.; Fan X. W. | |
2011 | |
发表期刊 | Thin Solid Films |
ISSN | 0040-6090 |
卷号 | 519期号:6页码:1976-1979 |
摘要 | Wurtzite Mg(x)Zn(1-x)O thin films were grown on sapphire substrates by low-pressure metal-organic chemical vapor deposition. The as-grown films show clear exciton absorption at room temperature until the composition x=0.25. A representative metal-semiconductor-metal structured photodetectors were fabricated from Mg(0.06)Zn(0.94)O film showed a peak responsivity of about 14.62 A/W at 340 nm, and the ultraviolet-visible rejection ratio (R340 nm/R400 nm) was more than two orders of magnitude at 3 V bias. The photodetector showed fast photoresponse with a rise time of 20 ns and a fall time of 400 ns. (C) 2010 Elsevier B.V. All rights reserved. |
收录类别 | SCI ; EI |
语种 | 英语 |
文献类型 | 期刊论文 |
条目标识符 | http://ir.ciomp.ac.cn/handle/181722/26035 |
专题 | 中科院长春光机所知识产出 |
推荐引用方式 GB/T 7714 | Zhao C. Y.,Wang X. H.,Zhang J. Y.,et al. Ultraviolet photodetector fabricated from metal-organic chemical vapor deposited MgZnO[J]. Thin Solid Films,2011,519(6):1976-1979. |
APA | Zhao C. Y..,Wang X. H..,Zhang J. Y..,Ju Z. G..,Shan C. X..,...&Fan X. W..(2011).Ultraviolet photodetector fabricated from metal-organic chemical vapor deposited MgZnO.Thin Solid Films,519(6),1976-1979. |
MLA | Zhao C. Y.,et al."Ultraviolet photodetector fabricated from metal-organic chemical vapor deposited MgZnO".Thin Solid Films 519.6(2011):1976-1979. |
条目包含的文件 | 下载所有文件 | |||||
文件名称/大小 | 文献类型 | 版本类型 | 开放类型 | 使用许可 | ||
Zhao-2011-Ultraviole(579KB) | 开放获取 | -- | 浏览 下载 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论