Highly Stable Core/Shell AgIn5S8/ZnS Quantum Dots for Pure White Light-Emitting Diodes

doi:10.1021/acsanm.3c04490

CIOMP OpenIR

	Highly Stable Core/Shell AgIn5S8/ZnS Quantum Dots for Pure White Light-Emitting Diodes
	Y. F. Sun, L. L. Zhang, Y. Lv, Q. H. Zeng, X. Y. Guo, W. Y. Ji and X. Y. Liu
	2023
发表期刊	Acs Applied Nano Materials
卷号	6 期号:23 页码:22311-22319
摘要	AgIn5S8/ZnS (AIS/ZS) core/shell quantum dots (QDs) have been synthesized using a hot injection method at relatively low temperature without any protection using inert gas. The QDs were characterized with UV visible electronic absorption spectroscopy, PL spectroscopy, Fourier transform infrared (FT-IR) spectroscopy, transmission electron microscopy (TEM), and temperature-dependent time-resolved PL (TRPL). The average size of the QDs was determined to be 1.73 +/- 0.29 nm. The QDs exhibit a major excitonic absorption band peaked at 479-573 nm and emission bands peaked from 548 to 666 nm with excitation at 410 nm with the peak position dependent on the synthesis temperature that affects the QD size. Upon the addition of trioctylphosphine (TOP) as a ligand, the PL quantum yield (PLQY) increased to 74.1% compared to 56.7% without TOP. The QDs show high stability after hours of ultraviolet (UV) light exposure or repetitive treatment with a significant amount of polar solvents, which is attributed to surface passivation by the ligands and ZnS shell. The luminescence mechanism of the core/shell AIS/ZS QDs is ascribed to donor-acceptor pair (DAP) recombination. TRPL results suggest that the binding energy of DAP increases and the DAP recombination probability is enhanced after passivation with TOP, leading to the high PLQY. Furthermore, prototype highly pure white light-emitting diodes (LEDs) based on these AIS/ZS QDs have been successfully demonstrated, yielding ideal 1931 CIE coordinates of (0.327, 0.335).
DOI	10.1021/acsanm.3c04490
URL	查看原文
收录类别	sci ; ei
语种	英语
引用统计
文献类型	期刊论文
条目标识符	http://ir.ciomp.ac.cn/handle/181722/67873
专题	中国科学院长春光学精密机械与物理研究所
推荐引用方式 GB/T 7714	Y. F. Sun, L. L. Zhang, Y. Lv, Q. H. Zeng, X. Y. Guo, W. Y. Ji and X. Y. Liu. Highly Stable Core/Shell AgIn5S8/ZnS Quantum Dots for Pure White Light-Emitting Diodes[J]. Acs Applied Nano Materials,2023,6(23):22311-22319.
APA	Y. F. Sun, L. L. Zhang, Y. Lv, Q. H. Zeng, X. Y. Guo, W. Y. Ji and X. Y. Liu.(2023).Highly Stable Core/Shell AgIn5S8/ZnS Quantum Dots for Pure White Light-Emitting Diodes.Acs Applied Nano Materials,6(23),22311-22319.
MLA	Y. F. Sun, L. L. Zhang, Y. Lv, Q. H. Zeng, X. Y. Guo, W. Y. Ji and X. Y. Liu."Highly Stable Core/Shell AgIn5S8/ZnS Quantum Dots for Pure White Light-Emitting Diodes".Acs Applied Nano Materials 6.23(2023):22311-22319.

条目包含的文件		下载所有文件
文件名称/大小	文献类型	版本类型	开放类型	使用许可
Highly Stable Core_S（2806KB）	期刊论文	出版稿	开放获取	CC BY-NC-SA	浏览下载