Effect of Ta addition on the microstructures and mechanical properties of in situ bi-phase (TiB2-TiCxNy)/(Ni-Ta) cermets

doi:10.1016/j.ceramint.2018.11.118

CIOMP OpenIR

	Effect of Ta addition on the microstructures and mechanical properties of in situ bi-phase (TiB2-TiCxNy)/(Ni-Ta) cermets
	H.Y.Yang; Z.Wang; S.L.Shu; J.B.Lu
	2019
发表期刊	Ceramics International
ISSN	0272-8842
卷号	45 期号:4 页码:4408-4417
摘要	In this work, in situ bi-phase (TiB2-TiCxNy)/(Ni-Ta) cermets were fabricated via a combined combustion synthesis and hot-pressing (CSHP) method in a Ni-Ti-BN-B4C-Ta system. The effects of Ta addition on the reaction process, phase constituents, microstructures and mechanical properties of the (TiB2-TiCxNy)/(Ni-Ta) cermets were studied. Ta is shown to dilute the system and lead to a small number of intermediate phases (Ni20Ti3B6 and Ni3Ti) that are retained in the products. Furthermore, the addition of Ta can markedly refine the ceramic particles and decrease the size and quantity of voids. The evaluation of the mechanical properties revealed that an increase in the Ta content resulted in increases in the compression strength (sigma(UCS)) and hardness and that the fracture strain (epsilon(f)) increased first and then decreased. The cermet with the optimal addition of 5 wt % Ta possessed the best mechanical properties without decreasing the value of epsilon(f) (2.9%). The addition of 5 wt% Ta resulted in a compressive strength of 3.37 GPa and the highest hardness of 1909 Hv, which is an increase of similar to 16% and similar to 22%, respectively, compared to cermets without added Ta.
关键词	Cermets,Ta content,Mechanical properties,high-temperature synthesis,combustion synthesis,high-strength,ti-c,compression properties,tantalum content,composites,behavior,zr,(ticxny-tib2)/ni,Materials Science
DOI	10.1016/j.ceramint.2018.11.118
收录类别	SCI ; EI
语种	英语
引用统计
文献类型	期刊论文
条目标识符	http://ir.ciomp.ac.cn/handle/181722/62881
专题	中国科学院长春光学精密机械与物理研究所
推荐引用方式 GB/T 7714	H.Y.Yang,Z.Wang,S.L.Shu,et al. Effect of Ta addition on the microstructures and mechanical properties of in situ bi-phase (TiB2-TiCxNy)/(Ni-Ta) cermets[J]. Ceramics International,2019,45(4):4408-4417.
APA	H.Y.Yang,Z.Wang,S.L.Shu,&J.B.Lu.(2019).Effect of Ta addition on the microstructures and mechanical properties of in situ bi-phase (TiB2-TiCxNy)/(Ni-Ta) cermets.Ceramics International,45(4),4408-4417.
MLA	H.Y.Yang,et al."Effect of Ta addition on the microstructures and mechanical properties of in situ bi-phase (TiB2-TiCxNy)/(Ni-Ta) cermets".Ceramics International 45.4(2019):4408-4417.

条目包含的文件		下载所有文件
文件名称/大小	文献类型	版本类型	开放类型	使用许可
Effect of Ta additio（5361KB）	期刊论文	出版稿	开放获取	CC BY-NC-SA	浏览下载