Efficient Blue-emitting Phosphor SrLu2O4 Ce3+ with High Thermal Stability for Near Ultraviolet (similar to 400 nm) LED-Chip based White LEDs

doi:10.1038/s41598-018-28834-8

CIOMP OpenIR

	Efficient Blue-emitting Phosphor SrLu2O4 Ce3+ with High Thermal Stability for Near Ultraviolet (similar to 400 nm) LED-Chip based White LEDs
	Zhang, S.; Hao, Z. D.; Zhang, L. L.; Pan, G. H.; Wu, H. J.; Zhang, X.; Luo, Y. S.; Zhang, L. G.; Zhao, H. F.; Zhang, J. H.
	2018
发表期刊	Scientific Reports
ISSN	2045-2322
卷号	8 页码:8
摘要	Blue-emitting phosphors for near ultraviolet (NUV) based tri-color RGB phosphor blend converted white light emitting diodes (LEDs) have been extensively investigated in the past few years. LED chip peaked near 400 nm is the most efficient among the NUV chips currently. However, most of blue phosphors show inefficient excitation around 400 nm. Herein, a novel blue phosphor SrLu2O4:Ce3+ matching well with near 400 nm chip and showing high thermal stability has been developed. The photoluminescence spectrum presents a broad emission band peaking at 460 nm with a bandwidth of nearly 90 nm. By optimizing the Ce3+ concentration, an internal quantum efficiency (IQE) as high as 76% was achieved. Furthermore, 86% of the room-temperature emission intensity is still maintained at 150 degrees C, indicating a good thermal stability and practicality. A series of white LEDs were fabricated based on 405 nm chips coated with a blend of the new blue phosphor with the commercial yellow and red phosphors. High color rendering indexes (>= 90) were achieved while the correlated color temperature was tuneable in the range of 3094 to 8990 K. These results suggest that SrLu2O4:Ce3+ can be utilized as a blue-emitting phosphor in NUV based white LEDs.
关键词	photoluminescence properties energy-transfer luminescence Science & Technology - Other Topics
DOI	10.1038/s41598-018-28834-8
收录类别	SCI
引用统计
文献类型	期刊论文
条目标识符	http://ir.ciomp.ac.cn/handle/181722/60646
专题	中国科学院长春光学精密机械与物理研究所
推荐引用方式 GB/T 7714	Zhang, S.,Hao, Z. D.,Zhang, L. L.,et al. Efficient Blue-emitting Phosphor SrLu2O4 Ce3+ with High Thermal Stability for Near Ultraviolet (similar to 400 nm) LED-Chip based White LEDs[J]. Scientific Reports,2018,8:8.
APA	Zhang, S..,Hao, Z. D..,Zhang, L. L..,Pan, G. H..,Wu, H. J..,...&Zhang, J. H..(2018).Efficient Blue-emitting Phosphor SrLu2O4 Ce3+ with High Thermal Stability for Near Ultraviolet (similar to 400 nm) LED-Chip based White LEDs.Scientific Reports,8,8.
MLA	Zhang, S.,et al."Efficient Blue-emitting Phosphor SrLu2O4 Ce3+ with High Thermal Stability for Near Ultraviolet (similar to 400 nm) LED-Chip based White LEDs".Scientific Reports 8(2018):8.

条目包含的文件		下载所有文件
文件名称/大小	文献类型	版本类型	开放类型	使用许可
Efficient Blue-emitt（2494KB）	期刊论文	出版稿	开放获取	CC BY-NC-SA	浏览下载