Changchun Institute of Optics,Fine Mechanics and Physics,CAS
Formation Mechanism of Strontium Hexaferrite Compounds by Complementary Structure and Thermogravimetry Investigations | |
Xu, L.![]() | |
2017 | |
发表期刊 | Nanoscience and Nanotechnology Letters
![]() |
卷号 | 9期号:4 |
摘要 | Strontium hexaferrite (SrFe12O19) compounds with hexagonal structure are fabricated by sintering the mixture of alpha-Fe2O3 and SrCO3 and ball milling the mixture of alpha-Fe2O3 and SrCO3 followed by heat treatment, respectively. The mechanism of formation of the SrFe12O19 in the two kinds of procedures was investigated by using both thermogravimetry and X-ray diffractometer measurements. It was found that the alpha-Fe2O3 reacted with SrCO3 to form SrFeO2.97 with cubic structure as the mixture was sintered above 750 degrees C firstly and then the SrFeO2.97 reacted with alpha-Fe2O3 to form SrFe12O19 in a sintering temperature ranging from 750 to 960 degrees C. However, the alpha-Fe2O3 reacted with SrCO3 to form Sr-containing Fe3O4 with spinel structure when the mixture was milled for 120 h, while the SrFe12O19 was obtained by annealing the Sr-containing Fe3O4 at 7001000 degrees C. The magnetic properties of the SrFe12O19 produced by the two kinds of procedures were reached. The saturation magnetization and the coercivity of the SrFe12O19 fabricated by ball milling followed by heat treatment were 60.65 emu/g and 5481.1 G, respectively, which were much larger than those of the SrFe12O19 produced by the other procedure. The mechanism leading to that the SrFe12O19 produced by the different methods had different magnetic properties was discussed in the present work. |
收录类别 | sci ; ei |
语种 | 英语 |
文献类型 | 期刊论文 |
条目标识符 | http://ir.ciomp.ac.cn/handle/181722/59351 |
专题 | 中科院长春光机所知识产出 |
推荐引用方式 GB/T 7714 | Xu, L.,H. Z. Wang,Y. Xu,et al. Formation Mechanism of Strontium Hexaferrite Compounds by Complementary Structure and Thermogravimetry Investigations[J]. Nanoscience and Nanotechnology Letters,2017,9(4). |
APA | Xu, L..,H. Z. Wang.,Y. Xu.,Q. H. Wang.,X. H. Ma.,...&Y. G. Zou and S. Xing.(2017).Formation Mechanism of Strontium Hexaferrite Compounds by Complementary Structure and Thermogravimetry Investigations.Nanoscience and Nanotechnology Letters,9(4). |
MLA | Xu, L.,et al."Formation Mechanism of Strontium Hexaferrite Compounds by Complementary Structure and Thermogravimetry Investigations".Nanoscience and Nanotechnology Letters 9.4(2017). |
条目包含的文件 | 下载所有文件 | |||||
文件名称/大小 | 文献类型 | 版本类型 | 开放类型 | 使用许可 | ||
Formation Mechanism (1355KB) | 期刊论文 | 作者接受稿 | 开放获取 | CC BY-NC-SA | 浏览 下载 |
个性服务 |
推荐该条目 |
保存到收藏夹 |
查看访问统计 |
导出为Endnote文件 |
谷歌学术 |
谷歌学术中相似的文章 |
[Xu, L.]的文章 |
[H. Z. Wang]的文章 |
[Y. Xu]的文章 |
百度学术 |
百度学术中相似的文章 |
[Xu, L.]的文章 |
[H. Z. Wang]的文章 |
[Y. Xu]的文章 |
必应学术 |
必应学术中相似的文章 |
[Xu, L.]的文章 |
[H. Z. Wang]的文章 |
[Y. Xu]的文章 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论