Microstructures and Tensile Properties of Al-Cu Matrix Composites Reinforced with Nano-Sized SiCp Fabricated by Semisolid Stirring Process
Qiu, F.; X. Gao; J. Tang; Y. Y. Gao; S. L. Shu; X. Han; Q. Li and Q. C. Jiang
2017
Source PublicationMetals
Volume7Issue:2
AbstractThe nano-sized SiCp/Al-Cu composites were successfully fabricated by combining semisolid stirring with ball milling technology. Microstructures were examined by an olympus optical microscope (OM), field emission scanning electron microscope (FESEM) and transmission electron microscope (TEM). Tensile properties were studied at room temperature. The results show that the alpha-Al dendrites of the composites were strongly refined, especially in the composite with 3 wt. % nano-sized SiCp, of which the morphology of the alpha-Al changes from 200 mu m dendritic crystal to 90 mu m much finer equiaxial grain. The strength and ductility of the composites are improved synchronously with the addition of nano-sized SiCp particles. The as-cast 3 wt. % nano-sized SiCp/Al-Cu composite displays the best tensile properties, i.e., the yield strength, ultimate tensile strength (UTS) and fracture strain increase from 175 MPa, 310 MPa and 4.1% of the as-cast Al-Cu alloy to 220 MPa, 410 MPa and 6.3%, respectively. The significant improvement in the tensile properties of the composites is mainly due to the refinement of the alpha-Al dendrites, nano-sized SiCp strengthening, and good interface combination between the SiCp and Al-Cu alloys.
Indexed Bysci ; ei
Language英语
Document Type期刊论文
Identifierhttp://ir.ciomp.ac.cn/handle/181722/59163
Collection中科院长春光机所知识产出
Recommended Citation
GB/T 7714
Qiu, F.,X. Gao,J. Tang,et al. Microstructures and Tensile Properties of Al-Cu Matrix Composites Reinforced with Nano-Sized SiCp Fabricated by Semisolid Stirring Process[J]. Metals,2017,7(2).
APA Qiu, F..,X. Gao.,J. Tang.,Y. Y. Gao.,S. L. Shu.,...&Q. Li and Q. C. Jiang.(2017).Microstructures and Tensile Properties of Al-Cu Matrix Composites Reinforced with Nano-Sized SiCp Fabricated by Semisolid Stirring Process.Metals,7(2).
MLA Qiu, F.,et al."Microstructures and Tensile Properties of Al-Cu Matrix Composites Reinforced with Nano-Sized SiCp Fabricated by Semisolid Stirring Process".Metals 7.2(2017).
Files in This Item: Download All
File Name/Size DocType Version Access License
Microstructures and (2488KB)期刊论文作者接受稿开放获取CC BY-NC-SAView Download
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Qiu, F.]'s Articles
[X. Gao]'s Articles
[J. Tang]'s Articles
Baidu academic
Similar articles in Baidu academic
[Qiu, F.]'s Articles
[X. Gao]'s Articles
[J. Tang]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Qiu, F.]'s Articles
[X. Gao]'s Articles
[J. Tang]'s Articles
Terms of Use
No data!
Social Bookmark/Share
File name: Microstructures and Tensile Properties.pdf
Format: Adobe PDF
This file does not support browsing at this time
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.