Synthesis of SnO2 nano-dodecahedrons with high-energy facets and their sensing properties to SO2 at low temperature

	Synthesis of SnO2 nano-dodecahedrons with high-energy facets and their sensing properties to SO2 at low temperature
	Ma, X. H.; Q. X. Qin; N. Zhang; C. Chen; X. Liu; Y. Chen; C. N. Li and S. P. Ruan
	2017
发表期刊	Journal of Alloys and Compounds
卷号	723
摘要	Dodecahedron-like SnO2 nanomaterial was synthesized via a solvothermal method under mild reaction condition. The morphological and structural characterization results indicated that the as-prepare dodecahedral SnO2 nanocrystallines with the average length of 130 nm and width of 45 nm were partially surrounded by high surface-energy {221} facets. The gas-sensing performance of the sample was investigated and the experiment results showed that the sensor had a good sensitivity to sulfur dioxide (SO2) at 183 degrees C. To 800 ppb SO2, the response could reach 1.32 and the response time was about 10 s. The good SO2-sensing performance of SnO2 nanocrystallines was closely related to the high surface-energy {221} facets whose surface possessed more dangling bonds and the corresponding SO2-sensing mechanism was discussed. (C) 2017 Elsevier B.V. All rights reserved.
收录类别	sci ; ei
语种	英语
文献类型	期刊论文
条目标识符	http://ir.ciomp.ac.cn/handle/181722/59131
专题	中科院长春光机所知识产出
推荐引用方式 GB/T 7714	Ma, X. H.,Q. X. Qin,N. Zhang,et al. Synthesis of SnO2 nano-dodecahedrons with high-energy facets and their sensing properties to SO2 at low temperature[J]. Journal of Alloys and Compounds,2017,723.
APA	Ma, X. H..,Q. X. Qin.,N. Zhang.,C. Chen.,X. Liu.,...&C. N. Li and S. P. Ruan.(2017).Synthesis of SnO2 nano-dodecahedrons with high-energy facets and their sensing properties to SO2 at low temperature.Journal of Alloys and Compounds,723.
MLA	Ma, X. H.,et al."Synthesis of SnO2 nano-dodecahedrons with high-energy facets and their sensing properties to SO2 at low temperature".Journal of Alloys and Compounds 723(2017).

条目包含的文件		下载所有文件
文件名称/大小	文献类型	版本类型	开放类型	使用许可
Synthesis of SnO2.pd（2380KB）	期刊论文	作者接受稿	开放获取	CC BY-NC-SA	浏览下载