Significantly enhancing the stability of a Cu2ZnSnS4 aqueous/ethanol-based precursor solution and its application in Cu2ZnSn(S,Se)(4) solar cells | |
Xiao, Z. Y.; Y. F. Li; B. Yao; Z. H. Ding; R. Deng; H. F. Zhao; L. G. Zhang and Z. Z. Zhang | |
2015 | |
发表期刊 | Rsc Advances |
卷号 | 5期号:125页码:103451-103457 |
摘要 | The stability of a CZTS precursor solution plays an important role for potential industrial applications, and could provide insight into the understanding of the solubility mechanism of the raw materials. In this work, we report a systematic investigation on the stability of a metal/thiourea aqueous/ethanol-based precursor solution used for fabricating Cu2ZnSnS4 (CZTS) thin films. It is found that the metal/thiourea aqueous/ethanol solution is metastable, and easily produced a mass of precipitation when the solution was prepared for few hours. This could cause an element to be missed out of the film, giving a very bad film-processing ability, and effect the application of such a method. So we studied in detail the crystalline precipitation through SEM, EDS and FTIR, and found that they mainly contain copper ion and thiourea coordination complexes. Furthermore, we demonstrated that the low-toxicity 3-mercaptopropionic acid (MPA) can play an important role as an auxiliary ligand in the precursor solution. Addition of MPA into the precursor solution can avoid the precipitation and noticeably improve the stability of the precursor solution from similar to 3 hours to 1 week. Using the precursor solution with added MPA, we fabricated a single phase of a CZTS film, and prepared a large-grain and hole-free Cu2ZnSn(S,Se)(4) (CZTSSe) film. More importantly, a CZTSSe film solar cell with a competitive power conversion efficiency of 7.25% has been reported in this work. |
收录类别 | SCI ; EI |
文献类型 | 期刊论文 |
条目标识符 | http://ir.ciomp.ac.cn/handle/181722/55485 |
专题 | 中科院长春光机所知识产出 |
推荐引用方式 GB/T 7714 | Xiao, Z. Y.,Y. F. Li,B. Yao,et al. Significantly enhancing the stability of a Cu2ZnSnS4 aqueous/ethanol-based precursor solution and its application in Cu2ZnSn(S,Se)(4) solar cells[J]. Rsc Advances,2015,5(125):103451-103457. |
APA | Xiao, Z. Y..,Y. F. Li.,B. Yao.,Z. H. Ding.,R. Deng.,...&L. G. Zhang and Z. Z. Zhang.(2015).Significantly enhancing the stability of a Cu2ZnSnS4 aqueous/ethanol-based precursor solution and its application in Cu2ZnSn(S,Se)(4) solar cells.Rsc Advances,5(125),103451-103457. |
MLA | Xiao, Z. Y.,et al."Significantly enhancing the stability of a Cu2ZnSnS4 aqueous/ethanol-based precursor solution and its application in Cu2ZnSn(S,Se)(4) solar cells".Rsc Advances 5.125(2015):103451-103457. |
条目包含的文件 | 下载所有文件 | |||||
文件名称/大小 | 文献类型 | 版本类型 | 开放类型 | 使用许可 | ||
Xiao-2015-Significan(808KB) | 期刊论文 | 作者接受稿 | 开放获取 | CC BY-NC-SA | 浏览 下载 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论