Decrease in particle size and enhancement of upconversion emission through Y3+ ions doping in hexagonal NaLuF4:Yb3+/Er3+ nanocrystals

	Decrease in particle size and enhancement of upconversion emission through Y3+ ions doping in hexagonal NaLuF4:Yb3+/Er3+ nanocrystals
	Xiang, G. T.; J. H. Zhang; Z. D. Hao; X. Zhang; G. H. Pan; Y. S. Luo and H. F. Zhao
	2015
发表期刊	Crystengcomm
卷号	17 期号:16 页码:3103-3109
摘要	The upconversion (UC) enhancement with size decrease has been realized through Y3+ ions doping in beta-NaLuF4:Yb3+/Er3+ nanocrystals (NCs) by a solvothermal process. X-Ray diffraction (XRD), scanning electron microscopy (SEM) and UC luminescence spectra were used to characterize the resulting samples. With an increase of the Y3+ doping concentration, the NCs size is continuously decreased with no phase transition. Meanwhile, the UC intensity is firstly increased and then it decreases when the Y3+ ions concentration is over 30 mol%. The NCs (beta-NaLu0.48Y0.3Yb0.2Er0.02F4) with the optimum Y3+ ions doping concentration (30 mol%) for UC emission have a diameter of about 80 nm. Compared with beta-NaLu0.78Yb0.2Er0.02F4 and beta-NaY0.78Yb0.2Er0.02F4 prepared under the same conditions, the green UC emission is enhanced by a factor of 1.8 and 16, respectively, for beta-NaLu0.48Y0.3Yb0.2Er0.0 F-2(4). The variation of the UC intensity with the increasing Y3+ ions concentration is attributed to the changing of the symmetry of the local crystal field induced by Y3+ ions doping, which has been proved by the structural probe Eu3+ ions. For beta-NaLu0.78Yb0.2Er0.02F4 and beta-NaLu0.48Y0.3Yb0.2Er0.02F4, a three-photon green UC process and a three-photon red UC process occur simultaneously at high pump power density, which can be described as (4)G(11)/(2) (Er3+) + I-4(15)/(2) (Er3+) -> H-2(11)/(2)/S-4(3)/(2) (Er3+) + I-4(13)/(2) (Er3+) and (4)G(11)/(2) (Er3+) + F-2(7)/(2) (Yb3+). F-4(9)/(2) (Er3+) + F-2(5)/(2) (Yb3+), respectively.
收录类别	SCI
文献类型	期刊论文
条目标识符	http://ir.ciomp.ac.cn/handle/181722/55480
专题	中科院长春光机所知识产出
推荐引用方式 GB/T 7714	Xiang, G. T.,J. H. Zhang,Z. D. Hao,et al. Decrease in particle size and enhancement of upconversion emission through Y3+ ions doping in hexagonal NaLuF4:Yb3+/Er3+ nanocrystals[J]. Crystengcomm,2015,17(16):3103-3109.
APA	Xiang, G. T.,J. H. Zhang,Z. D. Hao,X. Zhang,G. H. Pan,&Y. S. Luo and H. F. Zhao.(2015).Decrease in particle size and enhancement of upconversion emission through Y3+ ions doping in hexagonal NaLuF4:Yb3+/Er3+ nanocrystals.Crystengcomm,17(16),3103-3109.
MLA	Xiang, G. T.,et al."Decrease in particle size and enhancement of upconversion emission through Y3+ ions doping in hexagonal NaLuF4:Yb3+/Er3+ nanocrystals".Crystengcomm 17.16(2015):3103-3109.

条目包含的文件		下载所有文件
文件名称/大小	文献类型	版本类型	开放类型	使用许可
Xiang-2015-Decrease （2752KB）	期刊论文	作者接受稿	开放获取	CC BY-NC-SA	浏览下载