Effect of Mn, Fe and Co on the compression strength and ductility of in situ nano-sized TiB2/TiAl composites | |
Shu, S. L.; C. Z. Tong; F. Qiu and Q. C. Jiang | |
2015 | |
发表期刊 | Springerplus |
卷号 | 4页码:8 |
摘要 | The element of Fe can enhance the strength of TiB2/TiAl composite, but it is detrimental to the ductility of the composite due to the existence of large bulk TiB2 phase at grain boundary. The element of Mn is beneficial to the ductility of TiB2/TiAl composite, of which the fracture strain increases from 15.9 to 17.9 % with the addition of 2 at.% Mn. The element of Co can improve the strength and ductility of TiB2/TiAl composite simultaneously. With the addition of 2 at.% Co, the ultimate compression strength of TiB2/TiAl composite increases from 1829 to 1906 MPa and the fracture strain increases from 15.9 to 17.2 %. |
收录类别 | SCI |
WOS记录号 | BMC:10.1186/s40064-015-1575-5 |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | http://ir.ciomp.ac.cn/handle/181722/55398 |
专题 | 中科院长春光机所知识产出 |
推荐引用方式 GB/T 7714 | Shu, S. L.,C. Z. Tong,F. Qiu and Q. C. Jiang. Effect of Mn, Fe and Co on the compression strength and ductility of in situ nano-sized TiB2/TiAl composites[J]. Springerplus,2015,4:8. |
APA | Shu, S. L.,C. Z. Tong,&F. Qiu and Q. C. Jiang.(2015).Effect of Mn, Fe and Co on the compression strength and ductility of in situ nano-sized TiB2/TiAl composites.Springerplus,4,8. |
MLA | Shu, S. L.,et al."Effect of Mn, Fe and Co on the compression strength and ductility of in situ nano-sized TiB2/TiAl composites".Springerplus 4(2015):8. |
条目包含的文件 | 下载所有文件 | |||||
文件名称/大小 | 文献类型 | 版本类型 | 开放类型 | 使用许可 | ||
Shu-2015-Effect of M(1426KB) | 期刊论文 | 作者接受稿 | 开放获取 | CC BY-NC-SA | 浏览 下载 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论