GaSe:Er3+ crystals for SHG in the infrared spectral range

	GaSe:Er3+ crystals for SHG in the infrared spectral range
	Feng Z. S.; Guo J.; Xie J. J.; Zhang L. M.; Gao J. Y.; Andreev Y. M.; Izaak T. I.; Kokh K. A.; Lanskii G. V.; Shaiduko A. V.; Shabalina A. V.; Svetlichnyi V. A.
	2014
发表期刊	Optics Communications
ISSN	ISBN/0030-4018
期号	318 页码:205-211
摘要	Centimeter-sized Er-doped single crystals were grown from the melts GaSe:Er(0.025, 0.1, 0.5, 1 and 2 at%) by modified vertical Bridgman technology. Real Er content is ascertained as 0.009, 0.019, 0.033, 0.042 and 0.048 at%, respectively. Solubility of Er in GaSe does not exceed 5 x 10(-4). Optimal doping of 0.033 at% of Er was established from SHG experiment. Improved optical quality is identified as a reason of increased nonlinearity for about 24% to that in pure GaSe. New Raman scattering band is found at 2900 cm(-1) that properly related to F-4(9/2)-> I-4(9/2) transition of Er3+ ion. (C) 2013 Elsevier B.V. All rights reserved.
收录类别	SCI ; EI
语种	英语
文献类型	期刊论文
条目标识符	http://ir.ciomp.ac.cn/handle/181722/44011
专题	中科院长春光机所知识产出
推荐引用方式 GB/T 7714	Feng Z. S.,Guo J.,Xie J. J.,et al. GaSe:Er3+ crystals for SHG in the infrared spectral range[J]. Optics Communications,2014(318):205-211.
APA	Feng Z. S..,Guo J..,Xie J. J..,Zhang L. M..,Gao J. Y..,...&Svetlichnyi V. A..(2014).GaSe:Er3+ crystals for SHG in the infrared spectral range.Optics Communications(318),205-211.
MLA	Feng Z. S.,et al."GaSe:Er3+ crystals for SHG in the infrared spectral range".Optics Communications .318(2014):205-211.

条目包含的文件		下载所有文件
文件名称/大小	文献类型	版本类型	开放类型	使用许可
Feng-2014-GaSe_Er3+ （3114KB）			开放获取	CC BY-ND	浏览下载