Effects of surface modification and SiO2 thickness on the optical and superparamagnetic properties of the water-soluble ZnS:Mn2+ nanowires/Fe3O4 quantum dots/SiO2 heterostructures | |
Cao J.; Wang B. J.; Han D. L.; Yang S.; Yang J. H.; Wei M. B.; Fan L.; Liu Q. Y.; Wang T. T. | |
2013 | |
发表期刊 | Crystengcomm |
ISSN | ISBN/1466-8033 |
卷号 | 15期号:35 |
摘要 | In this paper, one-dimensional ZnS:Mn2+ nanowires (NWs)/Fe3O4 quantum dots (QDs)/SiO2 heterostructures were successfully synthesized by the Stober method to form the water-soluble fluorescent/superparamagnetic nanocomposites. The average diameter of the ZnS:Mn2+ NWs, Fe3O4 QDs and ZnS:Mn2+ NWs/Fe3O4 QDs/SiO2 heterostructures was about 6-8 nm, 4-5 nm and 18 nm, respectively. The Fe3O4 QDs were covalently linked to the ZnS:Mn2+ NWs by the conjugation of the hydroxyl groups on the surface of the QDs and the carboxyl groups modified on the surface of the NWs. It was found that the covalent bonds between the NWs and QDs could effectively suppress the energy transfer from the ZnS:Mn2+ NWs to the Fe3O4 QDs. As the SiO2 shell thickness increased, the fluorescence intensity reached the highest value when the hydrolysis time of tetraethyl orthosilicate was 5 hours, which was comparable to that of the ZnS:Mn2+ NWs. The superparamagnetic properties of the heterostructures were observed at room temperature, which decreased as the SiO2 thickness increased. |
收录类别 | SCI |
语种 | 英语 |
文献类型 | 期刊论文 |
条目标识符 | http://ir.ciomp.ac.cn/handle/181722/40632 |
专题 | 中科院长春光机所知识产出 |
推荐引用方式 GB/T 7714 | Cao J.,Wang B. J.,Han D. L.,et al. Effects of surface modification and SiO2 thickness on the optical and superparamagnetic properties of the water-soluble ZnS:Mn2+ nanowires/Fe3O4 quantum dots/SiO2 heterostructures[J]. Crystengcomm,2013,15(35). |
APA | Cao J..,Wang B. J..,Han D. L..,Yang S..,Yang J. H..,...&Wang T. T..(2013).Effects of surface modification and SiO2 thickness on the optical and superparamagnetic properties of the water-soluble ZnS:Mn2+ nanowires/Fe3O4 quantum dots/SiO2 heterostructures.Crystengcomm,15(35). |
MLA | Cao J.,et al."Effects of surface modification and SiO2 thickness on the optical and superparamagnetic properties of the water-soluble ZnS:Mn2+ nanowires/Fe3O4 quantum dots/SiO2 heterostructures".Crystengcomm 15.35(2013). |
条目包含的文件 | 下载所有文件 | |||||
文件名称/大小 | 文献类型 | 版本类型 | 开放类型 | 使用许可 | ||
Cao-2013-Effects of (1343KB) | 开放获取 | CC BY-NC-ND | 浏览 下载 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论