OPTICAL-PROPERTIES AND UP-CONVERTED EMISSIONS OF TM3+ IN YB3+ DOPED FLUOROPHOSPHATE GLASSES

	OPTICAL-PROPERTIES AND UP-CONVERTED EMISSIONS OF TM3+ IN YB3+ DOPED FLUOROPHOSPHATE GLASSES
	Ozen G.; Wu X.; Denis J. P.; Kermaoui A.; Pelle F.; Blanzat B.
	1993
发表期刊	Journal of Physics and Chemistry of Solids
ISSN	0022-3697
卷号	54 期号:11 页码:1533-1542
摘要	Optical properties of Tm3+ ions in Yb3+ doped fluorophosphate glasses containing 27 mole% PbF2 have been studied. The absorption, luminescence and excitation spectra, and the decay patterns were obtained as function of temperature, TmF3 and YbF3 concentrations. For the blue emission centered at 479 nm (1G4 --> H-3(6) transition) the critical concentration of Tm3+ is 0.2 mole% when the concentration of Yb3+ is kept constant at 20 mole%. The oscillator strengths of the transitions between J manifolds are calculated by using Judd-Ofelt theory at room temperature and were compared with the ones obtained experimentally. Radiative lifetimes of the excited states are determined and used to obtain nonradiative transition rates and the quantum yields. Upconverted emissions from the 1D2, 1G4 and F-3(4) levels were observed when the Yb3+ ions were excited with 966 nm light. An absolute upconversion efficiency for the blue (479 nm) and red (791 nm) emissions was obtained using a comparative method at room temperature. The efficiency of the 479 and 791 nm emissions was measured to be 5 x 10(-8) and 7 x 10(-4), respectively, for the sample containing 0.2 mole% TmF3 and 20 mole% YbF3 upon 966 nm excitation with an absorbed intensity of 20 mW cm-2. The emission intensity and the decay time of the 1G4 level were found to be independent of temperature although the emission intensity and the decay time of F-3(4) level show small temperature dependence when the desired level was directly excited. However, the upconverted emission intensity of these levels depends on temperature. This behaviour may be due to a phonon-assisted energy transfer mechanism from Yb3+ to Tm3+.
收录类别	SCI
语种	英语
文献类型	期刊论文
条目标识符	http://ir.ciomp.ac.cn/handle/181722/34378
专题	中科院长春光机所知识产出
推荐引用方式 GB/T 7714	Ozen G.,Wu X.,Denis J. P.,et al. OPTICAL-PROPERTIES AND UP-CONVERTED EMISSIONS OF TM3+ IN YB3+ DOPED FLUOROPHOSPHATE GLASSES[J]. Journal of Physics and Chemistry of Solids,1993,54(11):1533-1542.
APA	Ozen G.,Wu X.,Denis J. P.,Kermaoui A.,Pelle F.,&Blanzat B..(1993).OPTICAL-PROPERTIES AND UP-CONVERTED EMISSIONS OF TM3+ IN YB3+ DOPED FLUOROPHOSPHATE GLASSES.Journal of Physics and Chemistry of Solids,54(11),1533-1542.
MLA	Ozen G.,et al."OPTICAL-PROPERTIES AND UP-CONVERTED EMISSIONS OF TM3+ IN YB3+ DOPED FLUOROPHOSPHATE GLASSES".Journal of Physics and Chemistry of Solids 54.11(1993):1533-1542.

条目包含的文件		下载所有文件
文件名称/大小	文献类型	版本类型	开放类型	使用许可
bj01280335.pdf（3545KB）			开放获取	--	浏览下载