Preferred orientation of ZnO nanoparticles formed by post-thermal annealing zinc implanted silica

	Preferred orientation of ZnO nanoparticles formed by post-thermal annealing zinc implanted silica
其他题名	论文其他题名
	Liu Y. X.; Liu Y. C.; Shen D. Z.; Zhong G. Z.; Fan X. W.; Kong X. G.; Mu R.; Henderson D. O.
	2002
发表期刊	Solid State Communications
ISSN	0038-1098
卷号	121 期号:9—10 页码:531-536
摘要	High quality zinc oxide nanoparticles with (002) preferred orientation were prepared by post-thermal annealing zinc implanted silica at 700 degreesC using two methods. One method was annealing zinc implanted silica at 700 degreesC for 2 h in oxygen ambient; the other method was sequentially annealing zinc implanted silica at 700 degreesC in nitrogen and oxygen ambient for 1 h, respectively. X-ray diffraction (XRD), absorption and microphotoluminescence (micro-PL) results indicated that the latter method could create high quality ZnO nanoparticles with (002) preferred orientation and narrow size-distribution. X-ray photoelectron spectra (XPS) showed the formation of ZnO nanoparticles on a silica surface, where the ZnO nanoparticle content increased with increasing oxidation time in an oxygen environment. The processes of the transformation from Zn to ZnO are discussed. (C) 2002 Elsevier Science Ltd. All rights reserved.
收录类别	SCI ; EI
语种	英语
文献类型	期刊论文
条目标识符	http://ir.ciomp.ac.cn/handle/181722/26851
专题	中科院长春光机所知识产出
推荐引用方式 GB/T 7714	Liu Y. X.,Liu Y. C.,Shen D. Z.,et al. Preferred orientation of ZnO nanoparticles formed by post-thermal annealing zinc implanted silica[J]. Solid State Communications,2002,121(9—10):531-536.
APA	Liu Y. X..,Liu Y. C..,Shen D. Z..,Zhong G. Z..,Fan X. W..,...&Henderson D. O..(2002).Preferred orientation of ZnO nanoparticles formed by post-thermal annealing zinc implanted silica.Solid State Communications,121(9—10),531-536.
MLA	Liu Y. X.,et al."Preferred orientation of ZnO nanoparticles formed by post-thermal annealing zinc implanted silica".Solid State Communications 121.9—10(2002):531-536.

条目包含的文件		下载所有文件
文件名称/大小	文献类型	版本类型	开放类型	使用许可
Liu-2002-Preferred o（111KB）			开放获取	--	浏览下载