Photoluminescence characteristics of (Y,Gd)P0.5V0.5O4 : Tm3+ phosphor particles prepared by coprecipitation reaction | |
其他题名 | 论文其他题名 |
Lai H. S.; Chen B. J.; Xu W.; Wang X. J.; Yang Y. M.; Meng Q. Y. | |
2005 | |
发表期刊 | Journal of Alloys and Compounds
![]() |
ISSN | 0925-8388 |
卷号 | 395期号:1—2页码:181-184 |
摘要 | A novel blue-emitting material, fine-particle phosphor (Y,Gd)P0.5V0.5O4:Tm3+, has been prepared via co-precipitation reaction. The phosphor particles were characterized by XRD, SEM, and photoluminescence under vacuum ultraviolet (VUV, 147 nm) or ultraviolet (UV, 254 nm) excitation. The XRD patterns disclosed that (YGd)P0.5V0.5O4:Tm3+ particles calcined at 1200° C have the highest intensity. The SEM image showed that the size of the phosphor particles is uniform and submicron, and their morphology is regular and no agglomeration found. The fine particles blue-emitting material exhibits a narrow emission peak at 475 nm and a weak broad-band around 430 nm, whose intensity is dependent on the contents of TM3+ and VO43-. © 2004 Elsevier B.V. All rights reserved. |
收录类别 | SCI ; EI |
语种 | 英语 |
文献类型 | 期刊论文 |
条目标识符 | http://ir.ciomp.ac.cn/handle/181722/26821 |
专题 | 中科院长春光机所知识产出 |
推荐引用方式 GB/T 7714 | Lai H. S.,Chen B. J.,Xu W.,et al. Photoluminescence characteristics of (Y,Gd)P0.5V0.5O4 : Tm3+ phosphor particles prepared by coprecipitation reaction[J]. Journal of Alloys and Compounds,2005,395(1—2):181-184. |
APA | Lai H. S.,Chen B. J.,Xu W.,Wang X. J.,Yang Y. M.,&Meng Q. Y..(2005).Photoluminescence characteristics of (Y,Gd)P0.5V0.5O4 : Tm3+ phosphor particles prepared by coprecipitation reaction.Journal of Alloys and Compounds,395(1—2),181-184. |
MLA | Lai H. S.,et al."Photoluminescence characteristics of (Y,Gd)P0.5V0.5O4 : Tm3+ phosphor particles prepared by coprecipitation reaction".Journal of Alloys and Compounds 395.1—2(2005):181-184. |
条目包含的文件 | 下载所有文件 | |||||
文件名称/大小 | 文献类型 | 版本类型 | 开放类型 | 使用许可 | ||
Lai-2005-Photolumine(195KB) | 开放获取 | -- | 浏览 请求全文 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论