Changchun Institute of Optics,Fine Mechanics and Physics,CAS
Structure and luminescence properties of TiO2 : Er3+ nanocrystals annealed at different temperatures | |
其他题名 | 论文其他题名 |
Zhang J.; Wang X.; Zheng W. T.; Kong X. G.; Sun Y. J. | |
2007 | |
发表期刊 | Materials Letters |
ISSN | 0167-577X |
卷号 | 61期号:8—9页码:1658-1661 |
摘要 | Erbium doped TiO2 nanocrystals with the structures of anatase, pyrochlore Er2Ti2O7, and rutile, characterized by X-ray diffraction, have been obtained at different annealing temperatures from 300 degrees C to 900 degrees C. The nanocrystalline size for anatase TiO2 is reduced with increasing doped erbium concentration. Following ultraviolet 325 nm irradiation, the intensity of the green emission is the most intense for the TiO2:Er3+ nanocrystals with a structure of pyrochlore Er2Ti2O7, which evolves from the structure of anatase annealed at 800 degrees C. Moreover, following ultraviolet 325 nm and infrared 980 nm irradiation, the visible emission spectra for the nanocrystals annealed at 900 degrees C change drastically. Correspondingly, the structure of anatase disappears, while that of rutile becomes dominant, which indicates that phase transformation occurs. (c) 2006 Elsevier B.V. All rights reserved. |
收录类别 | SCI ; EI |
语种 | 英语 |
文献类型 | 期刊论文 |
条目标识符 | http://ir.ciomp.ac.cn/handle/181722/26620 |
专题 | 中科院长春光机所知识产出 |
推荐引用方式 GB/T 7714 | Zhang J.,Wang X.,Zheng W. T.,et al. Structure and luminescence properties of TiO2 : Er3+ nanocrystals annealed at different temperatures[J]. Materials Letters,2007,61(8—9):1658-1661. |
APA | Zhang J.,Wang X.,Zheng W. T.,Kong X. G.,&Sun Y. J..(2007).Structure and luminescence properties of TiO2 : Er3+ nanocrystals annealed at different temperatures.Materials Letters,61(8—9),1658-1661. |
MLA | Zhang J.,et al."Structure and luminescence properties of TiO2 : Er3+ nanocrystals annealed at different temperatures".Materials Letters 61.8—9(2007):1658-1661. |
条目包含的文件 | 下载所有文件 | |||||
文件名称/大小 | 文献类型 | 版本类型 | 开放类型 | 使用许可 | ||
Zhang-2007-Structure(299KB) | 开放获取 | -- | 浏览 下载 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论