Photoluminescence characteristics of Gd2Mo3O9 : Eu phosphor particles by solid state reaction method | |
其他题名 | 论文其他题名 |
Zhao X. X.; Wang X. J.; Chen B. J.; Meng Q. Y.; Di W. H.; Ren G. Z.; Yang Y. M. | |
2007 | |
发表期刊 | Journal of Rare Earths |
ISSN | 1002-0721 |
卷号 | 25期号:1页码:15-18 |
摘要 | Eu3+-doped Gd2Mo3O9 was prepared by solid-state reaction method using Na2CO3 as flux and characterized by powder X-ray diffractometry. According to X-ray diffraction, this material belonged to a tetragonal system with space group I4(1)/a. The effects of flux content and sintering temperature on the luminescent properties were investigated with the emission and excitation spectra. The results showed that flux content and sintering temperature had effects on the luminescent properties, the optimized flux content and the best temperature was 3% and 800 degrees C, respectively. The excitation and emission spectra also showed that this phosphor could be effectively excited by C-T band (280 nm), ultraviolet light 395 nm and blue light 465 rim. The wavelengths at 395 and 465 nm were nicely fitting in with the widely applied output wavelengths of ultraviolet or blue LED chips. Integrated emission intensity of Gd2Mo3O9 : Eu was twice higher than that of Y2O2S:Eu3+ under 395 nm excitation. The Eu3+ doped Gd2Mo3O9 phosphor may be a better candidate in solid-state lighting applications. |
收录类别 | SCI ; EI |
语种 | 英语 |
文献类型 | 期刊论文 |
条目标识符 | http://ir.ciomp.ac.cn/handle/181722/26618 |
专题 | 中科院长春光机所知识产出 |
推荐引用方式 GB/T 7714 | Zhao X. X.,Wang X. J.,Chen B. J.,et al. Photoluminescence characteristics of Gd2Mo3O9 : Eu phosphor particles by solid state reaction method[J]. Journal of Rare Earths,2007,25(1):15-18. |
APA | Zhao X. X..,Wang X. J..,Chen B. J..,Meng Q. Y..,Di W. H..,...&Yang Y. M..(2007).Photoluminescence characteristics of Gd2Mo3O9 : Eu phosphor particles by solid state reaction method.Journal of Rare Earths,25(1),15-18. |
MLA | Zhao X. X.,et al."Photoluminescence characteristics of Gd2Mo3O9 : Eu phosphor particles by solid state reaction method".Journal of Rare Earths 25.1(2007):15-18. |
条目包含的文件 | 下载所有文件 | |||||
文件名称/大小 | 文献类型 | 版本类型 | 开放类型 | 使用许可 | ||
Zhao-2007-Photolumin(361KB) | 开放获取 | -- | 浏览 下载 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论