Synthesis of colloidal LaF(3): 0.04Yb(3+), 0.01Er(3+) nanocrystals with green upconversion luminescence

	Synthesis of colloidal LaF(3): 0.04Yb(3+), 0.01Er(3+) nanocrystals with green upconversion luminescence
其他题名	论文其他题名
	Wang Y.; Qin W. P.; Zhang J. S.; Cao C. Y.; Jin Y.
	2008
发表期刊	Journal of Rare Earths
ISSN	1002-0721
卷号	26 期号:1 页码:40-43
摘要	A synthesis of LaF(3):0.04Yb(3+), 0.01Er(3+) nanocrystals with oleic acid as a capping ligand was presented. The X-Ray Diffraction (XRD) pattern indicated that the power was a single hexagonal phase. Transmission Electron Microscopy (TEM) demonstrated that the average size of the nanocrystals was less than 10 run, with a narrow size distribution. The nanocrystals were dispersible in nonpolar solvents and form a fully transparent colloidal solution, and the solution was stable for several months without any aggregates. The Yb(3+)-Er(3+) codoped nanocrystal colloidal solution exhibited a bright green upconversion fluorescence under 980 nm excitation from a diode laser. The nanocrystals were potentially applicable in biolabeling and bioimaging.
收录类别	SCI ; EI
语种	英语
文献类型	期刊论文
条目标识符	http://ir.ciomp.ac.cn/handle/181722/26498
专题	中科院长春光机所知识产出
推荐引用方式 GB/T 7714	Wang Y.,Qin W. P.,Zhang J. S.,et al. Synthesis of colloidal LaF(3): 0.04Yb(3+), 0.01Er(3+) nanocrystals with green upconversion luminescence[J]. Journal of Rare Earths,2008,26(1):40-43.
APA	Wang Y.,Qin W. P.,Zhang J. S.,Cao C. Y.,&Jin Y..(2008).Synthesis of colloidal LaF(3): 0.04Yb(3+), 0.01Er(3+) nanocrystals with green upconversion luminescence.Journal of Rare Earths,26(1),40-43.
MLA	Wang Y.,et al."Synthesis of colloidal LaF(3): 0.04Yb(3+), 0.01Er(3+) nanocrystals with green upconversion luminescence".Journal of Rare Earths 26.1(2008):40-43.

条目包含的文件		下载所有文件
文件名称/大小	文献类型	版本类型	开放类型	使用许可
Wang-2008-Synthesis （601KB）			开放获取	--	浏览下载