Low-temperature growth and optical properties of ZnO nanorods

	Low-temperature growth and optical properties of ZnO nanorods
其他题名	论文其他题名
	Yang J. H.; Lang J. H.; Yang L. L.; Zhang Y. U. J.; Wang D. D.; Fan H. G.; Liu H. L.; Wang Y. X.; Gao M.
	2008
发表期刊	Journal of Alloys and Compounds
ISSN	0925-8388
卷号	450 期号:1—2 页码:521-524
摘要	Zinc oxide (ZnO) nanorods were grown on ITO conducting glass by the chemical solution deposition method (CBD) in an aqueous solution that contained zinc nitrate hexahydrate (Zn(NO3)(2).6H(2)O) and methenamine (C6H12N4). The size of ZnO nanorods increased with molar concentration of zinc nitrate, and the nanorods with different aspect ratios also formed through tuning the reaction time when the molar concentration was 0.1 M. The length of nanorods increased significantly with the reaction time, but the thickness of the film deposited on the substrate only slightly increased. From the X-ray measurement results, it can be seen that the growth orientation of the as-prepared ZnO nanorods was [0 0 2]. Photoluminescence measurements were also carried out, the result showed a blue shift in violet emission with the reduction in crystal size. (C) 2007 Elsevier B.V. All rights reserved.
收录类别	SCI ; EI
语种	英语
文献类型	期刊论文
条目标识符	http://ir.ciomp.ac.cn/handle/181722/26362
专题	中科院长春光机所知识产出
推荐引用方式 GB/T 7714	Yang J. H.,Lang J. H.,Yang L. L.,et al. Low-temperature growth and optical properties of ZnO nanorods[J]. Journal of Alloys and Compounds,2008,450(1—2):521-524.
APA	Yang J. H..,Lang J. H..,Yang L. L..,Zhang Y. U. J..,Wang D. D..,...&Gao M..(2008).Low-temperature growth and optical properties of ZnO nanorods.Journal of Alloys and Compounds,450(1—2),521-524.
MLA	Yang J. H.,et al."Low-temperature growth and optical properties of ZnO nanorods".Journal of Alloys and Compounds 450.1—2(2008):521-524.

条目包含的文件		下载所有文件
文件名称/大小	文献类型	版本类型	开放类型	使用许可
Yang-2008-Low-temper（625KB）			开放获取	--	浏览下载