Synthesis and Optical properties of ZnO nanorods

	Synthesis and Optical properties of ZnO nanorods
其他题名	论文其他题名
	Lang J. H.; Yang J. H.; Li C. S.; Yang L.; Han Q.; Zhang Y. J.; Wang D. D.; Gao M.; Liu X. Y.
	2008
发表期刊	Crystal Research and Technology
ISSN	0232-1300
卷号	43 期号:12 页码:1314-1317
摘要	ZnO nanorods were prepared on the silicon (100) substrates using the chemical solution deposition method (CBD) without catalyst under a low temperature (90 degrees C). The cool water was used to dissolve the mixture of zinc nitrate hexahydrate (Zn (NO(3))(2)center dot 6H(2)O) and methenamine (C(6)H(12)N(4)) in order to decrease the size of ZnO nanorods. From the X-ray diffraction (XRD) results, it can be seen that the growth orientation of the as-prepared ZnO nanorods was (002). Scanning electron microscopy (SEM) results illustrated that the nanorods had a hexagonal wurzite structure and average diameter of about 120nm. The average diameter of nanorods prepared by the cool water process was much smaller than that by the room-temperature (RT) water process we always used. Photoluminescence (PL) measurements were also carried out. The result showed that a blue shift in UV emission band appeared in the PL spectrum of the sample grown with cool water process, which was mainly due to the reduction of tensile strain when the diameter of the ZnO nanorods decreased. (C) 2008 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim
收录类别	SCI ; EI
语种	英语
文献类型	期刊论文
条目标识符	http://ir.ciomp.ac.cn/handle/181722/26358
专题	中科院长春光机所知识产出
推荐引用方式 GB/T 7714	Lang J. H.,Yang J. H.,Li C. S.,et al. Synthesis and Optical properties of ZnO nanorods[J]. Crystal Research and Technology,2008,43(12):1314-1317.
APA	Lang J. H..,Yang J. H..,Li C. S..,Yang L..,Han Q..,...&Liu X. Y..(2008).Synthesis and Optical properties of ZnO nanorods.Crystal Research and Technology,43(12),1314-1317.
MLA	Lang J. H.,et al."Synthesis and Optical properties of ZnO nanorods".Crystal Research and Technology 43.12(2008):1314-1317.

条目包含的文件		下载所有文件
文件名称/大小	文献类型	版本类型	开放类型	使用许可
Lang-2008-Synthesis （155KB）			开放获取	--	浏览下载