Ultraviolet photodetector fabricated from metal-organic chemical vapor deposited MgZnO

	Ultraviolet photodetector fabricated from metal-organic chemical vapor deposited MgZnO
其他题名	论文其他题名
	Zhao C. Y.; Wang X. H.; Zhang J. Y.; Ju Z. G.; Shan C. X.; Yao B.; Zhao D. X.; Shen D. Z.; Fan X. W.
	2011
发表期刊	Thin Solid Films
ISSN	0040-6090
卷号	519 期号:6 页码:1976-1979
摘要	Wurtzite Mg(x)Zn(1-x)O thin films were grown on sapphire substrates by low-pressure metal-organic chemical vapor deposition. The as-grown films show clear exciton absorption at room temperature until the composition x=0.25. A representative metal-semiconductor-metal structured photodetectors were fabricated from Mg(0.06)Zn(0.94)O film showed a peak responsivity of about 14.62 A/W at 340 nm, and the ultraviolet-visible rejection ratio (R340 nm/R400 nm) was more than two orders of magnitude at 3 V bias. The photodetector showed fast photoresponse with a rise time of 20 ns and a fall time of 400 ns. (C) 2010 Elsevier B.V. All rights reserved.
收录类别	SCI ; EI
语种	英语
文献类型	期刊论文
条目标识符	http://ir.ciomp.ac.cn/handle/181722/26035
专题	中科院长春光机所知识产出
推荐引用方式 GB/T 7714	Zhao C. Y.,Wang X. H.,Zhang J. Y.,et al. Ultraviolet photodetector fabricated from metal-organic chemical vapor deposited MgZnO[J]. Thin Solid Films,2011,519(6):1976-1979.
APA	Zhao C. Y..,Wang X. H..,Zhang J. Y..,Ju Z. G..,Shan C. X..,...&Fan X. W..(2011).Ultraviolet photodetector fabricated from metal-organic chemical vapor deposited MgZnO.Thin Solid Films,519(6),1976-1979.
MLA	Zhao C. Y.,et al."Ultraviolet photodetector fabricated from metal-organic chemical vapor deposited MgZnO".Thin Solid Films 519.6(2011):1976-1979.

条目包含的文件		下载所有文件
文件名称/大小	文献类型	版本类型	开放类型	使用许可
Zhao-2011-Ultraviole（579KB）			开放获取	--	浏览下载