Pressure-induced crystallite breaking in La0.7Sr0.3Mn0.9Fe0.1O3 nanosolids

	Pressure-induced crystallite breaking in La0.7Sr0.3Mn0.9Fe0.1O3 nanosolids
其他题名	论文其他题名
	Zheng F. L.; Sui Y.; Xu D. P.; Su W. H.
	1998
发表期刊	Chinese Science Bulletin
ISSN	1001-6538
卷号	43 期号:6 页码:458-461
摘要	In the compacting process of the La0.7Sr0.3Mn0.9Fe0.1O3 nanosolids under the pressure range of 0.0-4.5 GPa, the apparent pressure-induced crystallite breaking phenomenon in these nanosolids was observed. With increasing pressure up to 4.5 GPa, the average grain size decreases by 46% while the magnetization of nanosolids decrease by 40% and their coercive increases by 35%. This kind of breaking has a close relation to the existence of oxygen deficiency in La0.7Sr0.3Mn0.9Fe0.1O3 nanoparticles. A simple and convenient method for preparing the bulk nanosolids with a large number of clean interfaces has been suggested.
收录类别	SCI
语种	英语
文献类型	期刊论文
条目标识符	http://ir.ciomp.ac.cn/handle/181722/25950
专题	中科院长春光机所知识产出
推荐引用方式 GB/T 7714	Zheng F. L.,Sui Y.,Xu D. P.,et al. Pressure-induced crystallite breaking in La0.7Sr0.3Mn0.9Fe0.1O3 nanosolids[J]. Chinese Science Bulletin,1998,43(6):458-461.
APA	Zheng F. L.,Sui Y.,Xu D. P.,&Su W. H..(1998).Pressure-induced crystallite breaking in La0.7Sr0.3Mn0.9Fe0.1O3 nanosolids.Chinese Science Bulletin,43(6),458-461.
MLA	Zheng F. L.,et al."Pressure-induced crystallite breaking in La0.7Sr0.3Mn0.9Fe0.1O3 nanosolids".Chinese Science Bulletin 43.6(1998):458-461.

条目包含的文件
文件名称/大小	文献类型	版本类型	开放类型	使用许可
Zheng-1998-Pressure-（347KB）			开放获取	--	浏览请求全文