Polymer-derived SiAlCN ceramics resist oxidation at 1400 C

	Polymer-derived SiAlCN ceramics resist oxidation at 1400 C
其他题名	论文其他题名
	Wang Y.; Fan Y.; Zhang L.; Zhang W.; An L.
	2006
发表期刊	Scripta Materialia
ISSN	13596462
卷号	55 期号:4 页码:295-297
摘要	The oxidation kinetics of polymer-derived SiAlCN ceramics are determined at 1400 C by measuring oxide-scale thickness as a function of oxidation time. The results reveal that the SiAlCN ceramics possess much better oxidation resistance than polymer-derived SiCN without Al, pure SiC and Si3N4. X-ray diffraction studies reveal that the oxide scales consist of cristobalite, plus a small amount of mullite for the sample with high aluminum-content. The reason that the SiAlCNs exhibited better oxidation resistance is discussed. 2006 Acta Materialia Inc.
收录类别	EI
文献类型	期刊论文
条目标识符	http://ir.ciomp.ac.cn/handle/181722/24546
专题	中科院长春光机所知识产出
推荐引用方式 GB/T 7714	Wang Y.,Fan Y.,Zhang L.,et al. Polymer-derived SiAlCN ceramics resist oxidation at 1400 C[J]. Scripta Materialia,2006,55(4):295-297.
APA	Wang Y.,Fan Y.,Zhang L.,Zhang W.,&An L..(2006).Polymer-derived SiAlCN ceramics resist oxidation at 1400 C.Scripta Materialia,55(4),295-297.
MLA	Wang Y.,et al."Polymer-derived SiAlCN ceramics resist oxidation at 1400 C".Scripta Materialia 55.4(2006):295-297.